日立金属・ＨＰＭ３１
平成 19年 3月分・山崎化学エイチ・ティでの熱処理変寸データです。# 単位は１コ、２コ
HPM31の実際の熱処理についてのご質問はこちらへどうぞ。
 |
|
|
| -0.03mm | -0.02mm | ±0.01mm | +0.02mm | +0.03mm | +0.04mm | +0.05mm | +0.10mm | |
| -25mm |
0 |
0 |
72 |
0 |
0 |
0 |
0 |
0 |
| -0.03mm | -0.02mm | ±0.01mm | +0.02mm | +0.03mm | +0.04mm | +0.05mm | +0.10mm | |
| 25-50mm |
0 |
1 |
19 |
3 |
0 |
0 |
0 |
0 |
| -0.03mm | -0.02mm | ±0.01mm | +0.02mm | +0.03mm | +0.04mm | +0.05mm | +0.10mm | |
| 50-75mm |
0 |
0 |
1 |
1 |
0 |
0 |
0 |
0 |
| -0.03mm | -0.02mm | ±0.01mm | +0.02mm | +0.03mm | +0.04mm | +0.05mm | +0.10mm | |
| 75-100mm |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
| -0.03mm | -0.02mm | ±0.01mm | +0.02mm | +0.03mm | +0.04mm | +0.05mm | +0.10mm | |
| 100-125mm |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
| -0.03mm | -0.02mm | ±0.01mm | +0.02mm | +0.03mm | +0.04mm | +0.05mm | +0.10mm | |
| 125-150mm |
0 |
1 |
0 |
0 |
0 |
0 |
0 |
0 |
| -0.03mm | -0.02mm | ±0.01mm | +0.02mm | +0.03mm | +0.04mm | +0.05mm | +0.10mm | |
| 150-175mm |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
| -0.03mm | -0.02mm | ±0.01mm | +0.02mm | +0.03mm | +0.04mm | +0.05mm | +0.10mm | |
| 175-200mm |
0 |
0 |
1 |
0 |
0 |
0 |
0 |
0 |
| -0.03mm | -0.02mm | ±0.01mm | +0.02mm | +0.03mm | +0.04mm | +0.05mm | +0.10mm | |
| 200-225mm |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
| -0.03mm | -0.02mm | ±0.01mm | +0.02mm | +0.03mm | +0.04mm | +0.05mm | +0.10mm | |
| 225-250mm |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
| -0.03mm | -0.02mm | ±0.01mm | +0.02mm | +0.03mm | +0.04mm | +0.05mm | +0.10mm | |
| 250-275mm |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
| -0.03mm | -0.02mm | ±0.01mm | +0.02mm | +0.03mm | +0.04mm | +0.05mm | +0.10mm | |
| 275-300mm |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
0 |
−- HPM31の山崎化学エイチ・ティでの熱処理特性 -−
SKD11と同等に方向性が大きく出る場合がある。
硬度的に DC53に次いで高温焼戻しに強い。
RIGOR STAVAX S-STAR DC53 PD613 HPM38 HPM31 SKD11